What is it?
Titanium Silicide
?
Titanium silicide, also known as TiSi2 or titanium disilicide, is a chemical compound with a molecular mass of 116.1333.
Titanium Silicide: What are its characteristics?
Titanium silicide TiSi2 (CAS 12039-383-7) has a high melting temperature, high corrosion resistance. High oxidation resistance. A binary alloy systemthe intermediate phase.
Titanium Silicide:
1. Preparing a titanium silicon silicide barrier, the device according to the method for creating the titanium silicide barriers layer. The invention eliminates silicideblock oxide layers in the prior art. This reduces costs and reduces loss of isolation oxide film through etching. It also improves stability.
2. A Ti5Si3 particles reinforced aluminum titan carbide (Ti3AlC2) matrix composite was made. A certain amount of titanium was added to Ti3AlC2/Ti5Si3 materials. These composite materials have different volume ratios, with a 10-40% volume percentage of the titanium-silicide particle reinforcing. The specific preparation method is as follows: first, using titanium powder, aluminum powder, silicon powder and graphite powder as raw materials, the molar ratio of Ti:Al:Si:C is 3:(1.1-x):x:(1.8~2.0), wherein x is 0.1~0.5. After mixing the raw powder by mechanical and physical methods for 824hrs, it is placed in a graphite mould with an applied pressure of 1020MPa. Next, the molar ratio Ti:Al.Si:C is 3 (1.1-x):x (1.82.0), wherein the temperature is 14001600. The sintering process takes 0.52hours, the sintering pressure 2040MPa. This invention is capable of preparing the aluminum titanium carbide/titaniumsilicide composite material with high purity, high strength and reduced time.
3. Preparation of functional titanium silicide coated glasses. The thin film can be deposited on a common glass substrate, or between them, a thin silicon film. You can make a composite of titanium silicide with silicon or add a little active carbon or Nitrogen to the film to create a composite of titanium silicide/titanium carbide, titanium nitride or composite silicon nitride. This will improve the mechanical strength as well as chemical resistance of the coated glasses. This new type of coated glass combines the functions dimming heat insulation as well as low radiation.
Titanium Silicide’s main supplier
Tech Co., Ltd. () is a professional silicide () Over 12 years’ experience in chemical products development and research. We accept credit cards, T/T and West Union payments. We will ship goods overseas via FedEx, DHL and by air or sea to our customers.
You can find high-quality powdered boron carbide here Please contact us Send an inquiry
Titanium Silicide: What are its characteristics?
Titanium silicide TiSi2 (CAS 12039-383-7) has a high melting temperature, high corrosion resistance. High oxidation resistance. A binary alloy systemthe intermediate phase.
| Titanium Silicide Property | |
| Other Titles | TiSi2 powder, titanium disilicide |
| No. | 12039-83-7 |
| Combination Formula | TiSi2 |
| Molecular Weight | 104.04 |
| Appearance | Black Powder |
| Melting Point | 1470 degC |
| Boiling Point | N/A |
| Density | 4.02 g/cm3 |
| Solubility of H2O | N/A |
| Exact Mass | 103.9018 |
Titanium Silicide Powder TiSi2 CAS 12039-83-7
1. Preparing a titanium silicon silicide barrier, the device according to the method for creating the titanium silicide barriers layer. The invention eliminates silicideblock oxide layers in the prior art. This reduces costs and reduces loss of isolation oxide film through etching. It also improves stability.
2. A Ti5Si3 particles reinforced aluminum titan carbide (Ti3AlC2) matrix composite was made. A certain amount of titanium was added to Ti3AlC2/Ti5Si3 materials. These composite materials have different volume ratios, with a 10-40% volume percentage of the titanium-silicide particle reinforcing. The specific preparation method is as follows: first, using titanium powder, aluminum powder, silicon powder and graphite powder as raw materials, the molar ratio of Ti:Al:Si:C is 3:(1.1-x):x:(1.8~2.0), wherein x is 0.1~0.5. After mixing the raw powder by mechanical and physical methods for 824hrs, it is placed in a graphite mould with an applied pressure of 1020MPa. Next, the molar ratio Ti:Al.Si:C is 3 (1.1-x):x (1.82.0), wherein the temperature is 14001600. The sintering process takes 0.52hours, the sintering pressure 2040MPa. This invention is capable of preparing the aluminum titanium carbide/titaniumsilicide composite material with high purity, high strength and reduced time.
3. Preparation of functional titanium silicide coated glasses. The thin film can be deposited on a common glass substrate, or between them, a thin silicon film. You can make a composite of titanium silicide with silicon or add a little active carbon or Nitrogen to the film to create a composite of titanium silicide/titanium carbide, titanium nitride or composite silicon nitride. This will improve the mechanical strength as well as chemical resistance of the coated glasses. This new type of coated glass combines the functions dimming heat insulation as well as low radiation.
Titanium Silicide’s main supplier
Tech Co., Ltd. () is a professional silicide () Over 12 years’ experience in chemical products development and research. We accept credit cards, T/T and West Union payments. We will ship goods overseas via FedEx, DHL and by air or sea to our customers.
You can find high-quality powdered boron carbide here Please contact us Send an inquiry